一、Q550CFC鋼板尺寸、外形、重量及允許偏差

鋼板的尺寸、外形、重量及允許偏差應(yīng)符合GB/T709的規(guī)定。

經(jīng)供需雙方協(xié)議，也可供應(yīng)其他尺寸、外形及允許偏差的鋼板

N類偏差：正偏差負偏差相等

A類偏差：按公稱厚度決定正偏差

B類偏差：固定負偏差為0.3

C類偏差：固定負偏差為0、按公稱厚度決定正偏差

二、Q550CFC鋼板執(zhí)行標(biāo)準(zhǔn)：YB/T4137-2013.

三、Q550CFC鋼板探傷：（Ⅰ、Ⅱ、Ⅲ級類探傷）

探傷：也叫超聲波檢驗，是針對鋼板內(nèi)部重量的一種檢驗方法及手段，可以檢驗港版的內(nèi)部缺陷。

根據(jù)需方要求，經(jīng)供需雙方協(xié)商，鋼板可進行超聲波檢測，檢測方法按GB/T2970或JB/T4730.3,檢驗方法和合格級別應(yīng)在合同中注明。

四、

Q550CFC steel plate smelting process

Steel is smelted in a converter or an electric furnace and shall be refined outside the furnace;The delivery state of Q550CFC steel plate shall be thermomechanically controlled rolling (TMCP), TMCP+ tempering or quenching + tempering (quenching and tempering). The specific delivery state shall be agreed by both parties and indicated in the contract.Steel plates shall be delivered by cutting or flame cutting

Note: Tempering and quenching analysis

Tempering: To hold the steel plate at a certain appropriate temperature for a long time before cooling

Quenching: is to heat the steel plate after heat preservation in water oil or other inorganic salts and other media for rapid cooling

五、Q550CFC鋼板化學(xué)成分

Q550CFC鋼的化學(xué)成分（熔煉分析）應(yīng)符合下表的規(guī)定（％）

Q550CFC化學(xué)成分要求

C

Si

Mn

P

S

Cr

Ni

Mo

V

Nb

Ti

B

≤0.09

≤0.5

≤2.0

≤0.02

≤0.01

≤0.8

≤1.8

≤0.7

≤0.1

≤0.12

≤0.05

≤0.005

六、Q550CFC鋼板焊接裂紋敏感性指數(shù)（不大于）Pcm/%

鋼牌號

產(chǎn)品厚度

名稱

≤50

50-60

60-75

75-100

Q550CFC

0.25

0.25

0.28

0.30

七、Q550CFC鋼板機械性能

Q550CFC的力學(xué)性能和工藝性能能應(yīng)符合下表規(guī)定：

Q550CFC力學(xué)性能要求（適用于橫向）

牌號

拉伸試驗

彎曲試驗

夏比V型沖擊試驗

上屈服強度

抗拉強度

斷后伸長率

彎曲1800

溫度

沖擊吸收能量

厚度≤50

50-100

Q550CFC

550

530

670-830

16

d=3a

0

60

八、Q550CFC鋼板沖擊功