型號：LEXAN 103 Resin

品名：PC

廠家：SABIC Innovative Plastics

特性：無鹵

用途：室外應(yīng)用

加工方法：注射成型

物理性能額定值單位制測試方法比重

ASTM D792--1.20g/cm3ASTM D792--1.19g/cm3ASTM D792特定體積0.835cm3/gASTM D792熔流率（熔體流動速率）(300°C/1.2 kg)7.0g/10 minASTM D1238收縮率 - 流動(3.20 mm)0.50 到 0.70%內(nèi)部方法吸水率

ASTM D57024 hr0.15%ASTM D570平衡, 23°C0.35%ASTM D570平衡, 100°C0.58%ASTM D570室外適用性f1

UL 746C硬度額定值單位制測試方法洛氏硬度

ASTM D785M 級70

ASTM D785R 級118

ASTM D785機械性能額定值單位制測試方法抗張強度1

ASTM D638屈服62.1MPaASTM D638斷裂65.5MPaASTM D638伸長率2

ASTM D638屈服7.0%ASTM D638斷裂110%ASTM D638彎曲模量3(50.0 mm 跨距)2340MPaASTM D790彎曲強度4(屈服, 50.0 mm 跨距)93.1MPaASTM D790泰伯耐磨性(1000 Cycles, 1000 g, CS-17 轉(zhuǎn)輪)10.0mgASTM D1044沖擊性能額定值單位制測試方法懸壁梁缺口沖擊強度(23°C)910J/mASTM D256無缺口懸臂梁沖擊(23°C)3200J/mASTM D4812落錘沖擊(23°C)169JASTM D3029拉伸沖擊強度5546kJ/m2ASTM D1822熱性能額定值單位制測試方法載荷下熱變形溫度

ASTM D6480.45 MPa, 未退火, 6.40 mm138°CASTM D6481.8 MPa, 未退火, 6.40 mm132°CASTM D648維卡軟化溫度154°CASTM D15256線形熱膨脹系數(shù) - 流動(-40 到 95°C)6.8E-5cm/cm/°CASTM E831比熱1260J/kg/°CASTM C351導(dǎo)熱系數(shù)0.19W/m/KASTM C177RTI Elec130°CUL 746RTI Imp130°CUL 746RTI130°CUL 746電氣性能額定值單位制測試方法體積電阻率> 1.0E+17ohms·cmASTM D257介電強度(3.20 mm, in Air)15kV/mmASTM D149介電常數(shù)

ASTM D15050 Hz3.17

ASTM D15060 Hz3.17

ASTM D1501 MHz2.96

ASTM D150耗散因數(shù)

ASTM D15050 Hz9.0E-4

ASTM D15060 Hz9.0E-4

ASTM D1501 MHz0.010

ASTM D150相比耐漏電起痕指數(shù)(CTI)PLC 2

UL 746高電弧燃燒指數(shù)(HAI)PLC 1

UL 746高電壓電弧起痕速率 (HVTR)PLC 2

UL 746熱絲引燃 (HWI)PLC 4

UL 746可燃性額定值單位制測試方法UL 阻燃等級(0.737 mm)HB

UL 94光學(xué)性能額定值單位制測試方法折射率1.586

ASTM D542透射率(2540 μm)88.0%ASTM D1003霧度(2540 μm)1.0%ASTM D1003注射額定值單位制

干燥溫度121°C

干燥時間3.0 到 4.0hr

干燥時間，48hr

建議的水分含量0.020%

建議注射量40 到 60%

料筒后部溫度288 到 310°C

料筒中部溫度299 到 321°C

料筒前部溫度310 到 332°C

射嘴溫度304 到 327°C

加工（熔體）溫度310 到 332°C

模具溫度